    Addition of benzalkonium chloride to self-adhesive resin-cements: Some clinically relevant properties
    (Informa Healthcare, 2014) Oğuz Ahmet, Serra; Mutluay, Mustafa Murat; Seyfio?lu Polat, Zelal; Seseoğulları-Dirihan, Roda; Bek, Bülent; Tezvergil-Mutluay, Arzu
    OBJECTIVE: The clinical survival rates of the adhesive restorations are limited due to the deterioration of resin-dentin bonds over time, partly due to the endogenous enzymatic activity of dentin. Recently, benzalkonium chloride (BAC) has been shown to effectively inhibit endogenous protease activity of dentin. This study evaluated the effect of different concentrations of benzalkonium chloride (BAC) on the degree of conversion (DC), vickers hardness (VH), setting time (ST) and biaxial flexural strength (FS) of two self-adhesive resin luting cements (RC).METHODS: Two RC SpeedCEM (Ivoclar-Vivadent) and BisCem (Bisco) were modified by addition of 0.1, 0.5, 1, 1.5, 2 wt% BAC. The luting cements without the addition of BAC served as control. The DC (FT-IR/ATR from the bottom of the resin disc), vickers hardness (from top and bottom of the light-cured specimen), setting time (ISO 4049) and biaxial flexural strength (0.6 × 6 mm discs) of the specimens were tested. Data were analyzed using ANOVA and Tukeys HSD.RESULTS: DC results were in the range of 70-80%, with some significant changes in BisCem (p < 0.05). VH values of both materials increased significantly compared to control, with no significant change as the BAC percentage increases. BAC addition influenced the ST differently for both materials. For BisCem, a gradual decrease (p < 0.05) was observed whereas, for SpeedCEM, a gradual increase was observed until 1% BAC (p < 0.05). For FS values, a gradual decrease was observed for both materials with increased amounts of BAC (p < 0.05), compared to the control group.CONCLUSIONS: BAC addition of up to 1% seems to be acceptable considering the properties tested. Clinical significance. Incorporation of benzalkonium chloride to self-adhesive resin luting cements during the mixing procedure does not significantly affect the degree of conversion or flexural strength of the luting agent and may be a good option to improve the durability of adhesive interface.
  • Küçük Resim
    Öğe
    Effect of gallic acid addition on some mechanical properties of self-adhesive resin cements
    (NLM (Medline), 2019) Oğuz Ahmet, Bebek Serra; Sayın Özel, Gülsüm; Mutluay, Mustafa Murat; Tezvergil-Mutluay, Arzu
    Self-adhesive resin cements (RCs) activate matrix metalloproteinase (MMP) and cathepsin-related collagen degradation, and gallic acid (GA) inhibits the activity of both MMPs and cysteine cathepsins. The purpose of this study was to evaluate the setting time, biaxial flexural strength, and Vickers hardness of self-adhesive RCs after the addition of two different concentrations of GA. RelyX U200 (3M ESPE) and Panavia SA (Kuraray) were modified with 0.5 and 1 wt% GA. The setting time of five samples in each RC group was assessed using a thermocouple apparatus as described in the ISO 4049 test. Biaxial flexure strength was measured using a universal testing machine until failure. Vickers hardness was measured with three randomized indentations on the surface of each resin disc. RCs without GA were used as control. Data were analyzed using a one-way analysis of variance and Tukey's HSD test (? = 0.05). The setting times ranged from 2.4 to 4.6 min for RelyX and from 4.9 to 6.0 min for Panavia. The biaxial flexure strength ranged from 76.5 to 109.7 MPa for RelyX and from 73.3 to 108.2 MPa for Panavia. Vickers hardness values ranged from 41.6 to 58.6 for RelyX and 27.2 to 33.6 for Panavia. The addition of 0.5 and 1 wt% GA to improve durability of resin-dentin bonds had no adverse effects on setting time, whereas the biaxial flexure strength and Vickers hardness values for the tested materials were significantly reduced.