Cyclic fatigue resistance of 2Shape, twisted file and EndoSequence xpress nickel-titanium rotary files at intracanal temperature

Abstract

Background. The aim of this study was to compare the cyclic fatigue resistance of 2Shape, Twisted File (TF) and EndoSequence Xpress (ESX) nickel-titanium rotary files at intracanal temperature (35°C). Methods. Twenty 2Shape TS1 (25/.04), 20 TF (25/.04) and 20 ESX (25/.04) files were tested for cyclic fatigue at intracanal temperature (35°C). All the instruments were rotated in artificial canals which were made of stainless steel with an inner diameter of 1.5 mm, 60° angle of curvature and a radius curvature of 5 mm until fracture occurred; the time to fracture was recorded in seconds using a digital chronometer and the number of cycles to fracture (NCF) for each file was calculated. Kruskal-Wallis test with Bonferroni correction was performed to statistically analyze data using SPSS 21.0. Statistical significance was set at P<0.05. Results. NCF values revealed that the 2Shape had significantly the highest cyclic fatigue resistance, followed by TF and ESX at intracanal temperature (P<0.05). The difference was significant between the TF and ESX groups (P<0.05). There was no significant difference among the 2Shape, TF and ESX files with respect to the lengths of the fractured file fragments (P>0.05). Conclusion. Within the limitations of present study, it was concluded that the cyclic fatigue resistance of 2Shape files at the intracanal temperature is higher than that of TF and ESX files.